VERBATIM PRIMALLOY Filament 1.75mm 500g - WHITE

VERBATIM PRIMALLOY Filament 1.75mm 500g - WHITE

Diameter accuracy 2.90 mm ± 0.05 mm 1.75 mm ± 0.05 mm
Process temperature 210 - 235 °C
Material N
Naša cena s DPH:
46,24 €
Naša cena bez DPH:
38,54 €

ks
Bežná cena:
58,67 €
Ušetríte:
12,43 €
Zľava:
21,17%
Výrobca:
Verbatim
Dostupnosť:
Skladom ext.
Katalógové číslo:
408243
Záruka:
2 roky
Nákup na splátky:
Quatro kalkulačka Splátková kalkulačka



Popis tovaru


Diameter accuracy 2.90 mm ± 0.05 mm 1.75 mm ± 0.05 mm

Process temperature 210 - 235 °C

Material Net Weight 500 g

Filament Length 70 m (2.85mm thickness) 190 m (1.75mm thickness)

Density 1.08 – 1.10 g/cm3

Tensile Yield (JIS K 7113) 14 MPa

Elongation (JIS K 7113) 990 %

Melting Point 175 to 195 °C

Melt Flow Index @ 230 °C, 21.1N 45 g/(10 minutes)

Durometer Hardness D (JIS K 6253) 33

Material Grade MCC TPE-33

For use in commonly available fused fi lament fabrication (FFF) 3D printers. Not recommended for printers with signifi cant distance (e.g. >15 mm) between pinch feeder and hot end. Best results obtained with printers having a heated platform and whenapplying forced air cooling on the object as it builds.

PRIMALLOY
Verbatim will expand its portfolio of fi laments to include exclusive products developed by Mitsubishi Chemical. The fi rst of these special fi laments to be marketed and distributed by Verbatim is PRIMALLOY™. It produces objects with a rubberised feel which will have possible usage for things like hand grips for tools, earphones, goggles, mobile phone cases, automotive parts, and many more. It is a thermoplastic ester elastomer (TPE) which consists of a crystalline aromatic polyester block (mainly PBT) as the hard segment, and an uncrystalline polyether block (mainly poly-tetramethylene-ether-glycol) as the soft segment. The features of PRIMALLOY™ include good mechanical strength, oil resistance, chemical resistance, fl ex fatigue resistance and has excellent heat resistance, as well as hardness stability within a wide temperature range.